PA (Polyamide)

Kunststoff-Rundstangen PA (Polyamide) ■ Lagerlängen: PA 6 xt, PA 6.6, PA 6.6-30GF: 1000 mm/ 2000 mm PA 6 G: 50 – 200 = 1000 mm / 2000 mm 220 – 500 = 1000 mm ■ Farben: = natur ; = schwarz

kunststoff_pa_vollstaebe_1

Durchmesser in mm	PA 6 xt kg/mtr.	PA 6.6 kg/mtr.	PA 6.6-30GF kg/mtr.	PA 6 G kg/mtr.
6	0,035	0,035
8	0,063	0,063
10	0,096	0,096
12	0,141	0,141
15	0,217
16	0,246	0,246
18	0,309
20	0,380	0,380	0,450
22	0,462
25	0,595	0,595	0,705
28	0,740
30	0,850	0,850	1,007
36	1,220	1,220
40	1,500	1,500	1,778
45	1,910	1,910
50	2,350	2,350	2,785	2,390
56	2,930
60	3,380	3,380	4,005	3,440
65	3,950
70	4,640	4,640	5,498	4,800

kunststoff_pa_vollstaebe_2

Durchmesser in mm	PA 6 xt kg/mtr.	PA 6.6 kg/mtr.	PA 6.6-30GF kg/mtr.	PA 6 G kg/mtr.
75	5,300
80	6,050	6,050	7,169	6,200
85	6,850
90	7,670	7,670		7,800
100	9,450	9,450	11,198	9,800
110	11,500			11,700
120	13,700		16,235	14,200
125
130	16,100	16,100		16,900
140	18,700			20,000
150	21,400	21,400	25,359	22,500
160				25,100
170				28,400
180	30,800			31,500
200	38,100			39,200
220				48,000
230				50,600
250				59,800
280				75,800
300				87,800
320				101,500

Produktinformationen:

Dieser teilkristalline Werkstoff wird, aufgrund seiner guten thermischen und mechanischen Eigenschaften zur der Polymer-Gruppe der technischen Kunststoffe gezählt. Er besitzt, neben der hohen Festigkeit, Härte und Zähigkeit eine hohe Wärmeformbeständigkeit von -40 °C bis ca. +100 °C. Das gute Dämpfungsvermögen kann aber erst nach einer Konditionierung erreicht werden, daher sollte dieser Werkstoff nach einer Temperung erneut konditioniert werden. Der Werkstoff verfügt zudem über gute Gleit- und Notlaufeigenschaften. Durch das gesteigerte Feuchtigkeitsaufnahmeverhalten im Vergleich zu anderen polymeren Werkstoffen müssen mögliche Dimensionsänderungen, sowie Änderungen der Mechanik und der elektrischen Eigenschaften im Vorfeld berücksichtigt werden.